PA12-CF Filament
PA12-CF Filament

PA12-CF Filament

Regular price$99.00
/
Shipping calculated at checkout.

Product Features

  • Superior Strength and Stiffness

  • Toughness & Vibration Resistance

  • Exceptional Thermal Resistance

  • Comes with High Temperature Spool

  • Diameter: 1.75mm +/- 0.02mm

Cautions for Use

  • 0.2 mm Nozzle Not Compatible

  • Brass/Copper plated Nozzle Not Recommended

  • Dry before Use

  • Enclosure Printer Required

Ship From
  • In stock, ready to ship
  • Inventory on the way


QIDI PA12-CF 3D Printer Filament

It greatly improves the mechanical properties and heat resistance of the material, and releases the internal stress during the printing process through the fiber mesh structure, resulting in good dimensional stability of the printed part and no warpage.

PA12-CF PA12-CF


Temperature and Humidity Resistance

QIDI TECH PAHT-CF(PPA-CF) Filament's have good tensile and flexural strength performance in both wet and dry environments.

PA12-CF PA12-CF PA12-CF



Display of PA12-CF Prints

QIDI PA12-CF has a low coefficient of friction, self-lubricating properties and excellent wear resistance, which can easily meet all kinds of high-strength gears or industrial applications with high wear requirements.


PA12-CF PA12-CF



Accessory Compatibility

Recommended Not Recommended
Build Plate QIDI PEI Plate, HF Plate and Smooth Plate PC Plate
Hotend Hardened Steel Nozzle ( 0.4 / 0.6 / 0.8 mm)
Bimetal Nozzle ( 0.4 / 0.6 / 0.8 mm)
Brass/Copper plated Nozzle (0.2/0.4/0.6/0.8 mm)
Glue PVP glue/ 3D LAC adhesive spray /
Recommended Printing Settings
Drying Settings (Blast Drying Oven) 80-100 °C,4-6 h
Printing and Keeping Container's Humidity < 15% RH (Sealed, with Desiccant)
Nozzle Temperature 280 - 300 °C
Bed Temperature (with Glue) 40-70 °C
Printing Speed < 30-120 mm/s
Physical Properties
Density 1.09 g/cm³
Water absorption 2.46 %
Heat Deflection Temperature 78.4 °C
Melting Temperature 167 °C
Melt Index 5.1 g/10 min
Mechanical Properties
Tensile Strength 76.95±1.17 MPa
Breaking Elongation Rate 1.63±0.10 %
Bending Modulus 3915.93±195.30 MPa
Bending Strength 114.12±1.93 MPa
Impact Strength 10.01±0.83 KJ/m2



Printing Tips

• PA12-CF material is very sensitive to moisture. Printing after absorbing moisture will result in ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the QIDI PAHT-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
• After the printing, the printed part can be annealed to further improve the strength of QIDI PAHT-CF print part. Annealing conditions: place the printed part at 80-100°C for 4-6 hours and cool to room temperature naturally.
For more details please refer to: Filament Guide on WIKI.


Vacuum Aluminum Foil Packaging

According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant.

PA12-CF PA12-CF

Product Size

QIDI TECH PA12-CF filament 1.75mmWorks perfectly with most FDM 3Dprinters on the market.

PA12-CF PA12-CF
PA12-CF PA12-CF
PA12-CF