Name: UltraPA Nylon Filament (PPA)
Brand: Qidi Tech
SKU: NYLON001
Price: 102.0 CAD
Availability: InStock

$102.00

Product Features

Low Moisture Sensitivity
Strongest layer bonding performance
Super Abrasive Resistance
Exceptional Thermal Resistance
Comes with High Temperature Spool
Diameter: 1.75mm +/- 0.02mm

Cautions for Use

Brass Nozzle Not Recommended
Dry before Use
Enclosed Printer Required
Active chamber heating recommended

In stock, ready to ship
Backordered, shipping soon

Quantity

Shipping rates vary by locations. See our Shipping policy for details.

QIDI UltraPA 3D Printer Filament

QIDI UltraPA is specially developed for FDM 3D printing process, and its substrate material is high temperature nylon（PPA）, which has low density, low moisture absorption, high strength, high abrasion resistance, excellent chemical resistance and high heat resistance.

Low Moisture Sensitivity

QIDI TECH UltraPA based on modified high temperature nylon（substrate material：PPA）, whose saturated moisture absorption rate is only one fifth of ordinary PA6, completely solving the defects of the mechanical properties and dimensional stability of nylon materials that change greatly after absorbed moisture.

Strongest layer bonding performance

QIDI UltraPA have the best layer strength,the layer adhesion of single wall structure is 2-3 times of ABS material and 1.5 times of PLA material.

Super Abrasive Resistance

QIDI UltraPA has low coefficient of friction, self-lubricating properties and excellent wear resistance,which can easily meet all kinds of high-strength gears or industrial applications with high wear requirements.

Accessory Compatibility

	Recommended	Not Recommended
Build Plate	QIDI PEI Plate, HF Plate and Smooth Plate	PC Plate
Hotend	Hardened Steel Nozzle ( 0.4 / 0.6 / 0.8 mm) Bimetal Nozzle ( 0.4 / 0.6 / 0.8 mm)	Brass/Copper plated Nozzle (0.2/0.4/0.6/0.8 mm)
Glue	PVP glue/ 3D LAC adhesive spray	/

Recommended Printing Settings
Drying Settings (Blast Drying Oven)	80-100 °C，4-6 h
Printing and Keeping Container's Humidity	< 15% RH (Sealed, with Desiccant)
Nozzle Temperature	260 - 280 °C
Bed Temperature (with Glue)	70-80 °C
Printing Speed	< 30-120 mm/s

Physical Properties
Density	1.21 g/cm³
Water absorption	2.10 %
Heat Deflection Temperature	72.5 °C
Melting Temperature	231 °C
Melt Index	9.4 g/10 min

Mechanical Properties
Tensile Strength	69.29±1.17 MPa
Breaking Elongation Rate	9.77±1.68 %
Bending Modulus	3202.24±115.78 MPa
Bending Strength	112.64±1.60 MPa
Impact Strength	9.74±0.84 KJ/m2

Downloads

Filament TDS

Filament MSDS

Printing Tips

• Nylon material is very sensitive to moisture. Printing after absorbing moisture will result in ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the QIDI PAHT-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
• After the printing, the printed part can be annealed to further improve the strength of QIDI PAHT-CF print part. Annealing conditions: place the printed part at 80-100°C for 4-6 hours and cool to room temperature naturally.
For more details please refer to: Filament Guide on WIKI.

Vacuum Aluminum Foil Packaging

According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant.