Product Features

  • Very Low Moisture Absorption

  • Exceptional Mechanical Properties

  • High Dimensional Stability

  • Exceptional Thermal Resistance

  • Comes with High Temperature Spool

  • Diameter: 1.75mm +/- 0.02mm

Cautions for Use

  • 0.2 mm Nozzle Not Compatible

  • Brass/Copper plated Nozzle Not Recommended

  • Dry before Use

  • Enclosed printer (Recommended)

Weight
Ship From
  • 在庫あり、発送準備完了
  • 途中の在庫

QIDI PET-CF 3D Printer Filament

QIDI PET-CF is specially developed for FDM 3D printing process, and its substrate material is PET engineering plastic with low moisture absorption, high strength, creep resistance, excellent chemical resistance and high heat resistance. With good dimensional stability, no warpage and no shrinkage and no smell, no heating chamber are required during the printing process. It can be used with QIDI S-White Support Material to solve the problem of poor molding effect of supporting surface of complex model.

PET-CF PET-CF

PET-CF PET-CF


Smooth High-speed Printing

QIDI PET-CF Filaments prints out models with great gloss and beautiful texture.






PET-CF PET-CF

Smart Fiber Reinforced Technology

QIDI Smart Fiber Reinforcement Technology significantly improves the mechanical properties and heat resistance of the material and releases internal stresses through the fiber mesh structure during the printing process, resulting in good dimensional stability of the printed part without warping.

PET-CF PET-CF

Low Creep

The molecular chain structure of PET is highly regular and has a rigid benzene ring structure, so that PET has better mechanical properties and less deformation under long-term load. Compared with PA and PC materials, PET has better creep-resistance.


PET-CF PET-CF06

High Mechanical Strength

PET filament carbon fiber has higher strength and rigidity, Better impact Resistance,and Wear Resistance than regular PETG material.Suitable for applications requiring torsional, tensile, and impact strength.

PET-CF PET-CF07

Low Moisture Absorption

QIDI PET-CF has the characteristics of low moisture absorption, and the moisture absorption of this carbon fiber reinforced PET is only 0.5%.Moisture has no effect on the mechanical properties and dimensional stability of QIDI PET-CF.




Accessory Compatibility

Recommended Not Recommended
Build Plate QIDI PEI Plate, HF Plate and Smooth Plate PC Plate
Hotend Hardened Steel Nozzle ( 0.4 / 0.6 / 0.8 mm)
Bimetal Nozzle ( 0.4 / 0.6 / 0.8 mm)
Brass/Copper plated Nozzle (0.2/0.4/0.6/0.8 mm)
Glue Glue Stick/ 3D LAC adhesive spray /
Recommended Printing Settings
Drying Settings (Blast Drying Oven) 100 °C,4-8 h
Printing and Keeping Container's Humidity < 15% RH (Sealed, with Desiccant)
Nozzle Temperature 280 - 320 °C
Bed Temperature (with Glue) 80 °C
Printing Speed < 30-120 mm/s
Physical Properties
Density 1.3 g/cm³
Vicat Softening Temperature 148.8 °C
Heat Deflection Temperature 86.7 °C
Melting Temperature 251 °C
Melt Index 6.8 g/10 min
Mechanical Properties
Tensile Strength 72.51±1.39 MPa
Breaking Elongation Rate 2.49±0.22 %
Bending Modulus 5345.71±231.24 MPa
Bending Strength 114.47±1.89 MPa
Impact Strength 7.75±1.08 kJ/m²



Printing Tips

• Although the moisture absorption of PET material is very low, it is very sensitive to moisture. Printing after absorbing moisture will result in ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the QIDI PET-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
• After the printing, the printed part can be annealed to further improve the strength of QIDI PET-CF print part. Annealing conditions: place the printed part at 80-100°C for 4-8 hours and cool to room temperature naturally.
For more details please refer to: Filament Guide on WIKI.


Vacuum Aluminum Foil Packaging

According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant.

PET-CF PET-CF

Product Size

QIDI TECH PET-CF filament 1.75mmWorks perfectly with most FDM 3Dprinters on the market.

PET-CF PET-CF
PET-CF PET-CF